Stakalloy is a ternary alloy of uranium composed of vanadium, niobium, and depleted uranium. The alloy was developed in 2002 by Michael R. Staker of Loyola University Maryland under grant from the United States Army.
Composition
The niobium content of stakalloy is between 0.01 and 0.95 percent by weight and the balance being uranium. The vanadium content of the alloy is between the gamma eutectoid and the eutectic compositions, 1.0 percent and 4.5 percent by weight respectively.Properties
Stakalloy has improved metallurgical properties over other depleted uranium alloys, such as staballoy, being more viable as a structural alloy where a combination between high strength and high density is required. Changes include that of density, hardness, ballistic properties, and machinability.Production
Staker's invention of stakalloy involved reducing excessive carbon levels while adding together uranium with trace amounts of niobium and vanadium. The three constituent parts may be combined through melting, however, the niobium and vanadium must be charged into the melt or introduced to additional melt stock before heat-up.Arc melting is also a melting technique noted by Staker, in which niobium is added to an alloy of vanadium and uranium from a crucible.
After casting an ingot of stakalloy, the ingot can be used in the as-cast condition or be worked—either hot or cold—to change both properties and shape. Stakalloy can also be heat-treated after manipulation of shape.