Carbon steel


Carbon steel or non-alloy steel is a steel with carbon content from about 0.05 up to 2.1 percent by weight. The definition of carbon steel from the American Iron and Steel Institute states:
The addition of significant amounts other metals such as nickel, chromium, vanadium, molybdenum change the materials definition from carbon steel alloy steel.
As the carbon content percentage rises, steel has the ability to become harder and stronger through heat treating; however, it becomes less ductile. Regardless of the heat treatment, a higher carbon content reduces weldability. In carbon steels, the higher carbon content lowers the melting point.
High-carbon steel has many uses primarily applications where medium strength and low material cost are factors, these include: high strength steel wires, springs, bolts, garden and agricultural tools, wood chisels, axes etc.

Properties

Carbon steel is often divided into two main categories: low-carbon steel and high-carbon steel. It may also contain other elements, such as manganese, phosphorus, sulfur, and silicon, which can affect its properties. C
Low carbon steel can be easily machined and welded, making it versatile and suitable for various applications which require reasonable strength and low material cost such as car body panels, footbridges, hand rails, garden furniture/park benches, nails, gates etc. Higher carbon is less easily machined and is much less suitable for welding It can also be heat treated to improve its strength, hardness, and durability.
Carbon steel is susceptible to rust and corrosion, especially in environments with high moisture levels and/or salt. It can be shielded from corrosion by coating it with paint, varnish, or other protective material. Alternatively, it can be made from a stainless steel alloy that contains chromium, which provides excellent corrosion resistance. Carbon steel can be alloyed with other elements to improve its properties, such as by adding chromium and/or nickel to improve its resistance to corrosion and oxidation or adding molybdenum to improve its strength and toughness at high temperatures.
It is an environmentally friendly material, as it is easily recyclable and can be reused in various applications. It is energy-efficient to produce, as it requires less energy than other metals such as aluminium and copper.

Type

Mild or low-carbon steel

Mild steel, also known as plain-carbon steel and low-carbon steel, is now the most common form of steel because its price is relatively low while it provides material properties that are acceptable for many applications. Mild steel contains approximately 0.05–0.30% carbon making it malleable and ductile. Mild steel has a relatively low tensile strength, but it is cheap and easy to form. Surface hardness can be increased with carburization.
The density of mild steel is approximately and the Young's modulus is.
Low-carbon steels display yield-point runout where the material has two yield points. The first yield point is higher than the second and the yield drops dramatically after the upper yield point. If a low-carbon steel is only stressed to some point between the upper and lower yield point then the surface develops Lüder bands. Low-carbon steels contain less carbon than other steels and are easier to cold-form, making them easier to handle. Typical applications of low carbon steel are car parts, pipes, construction, and food cans.

High-tensile steel

Steels which have a carbon content above ~0.3% can have their hardness and tensile strength modified by heat treatment. Heating to approxmately 850c followed by rapid cooling/quenching in water or oil increases hardness and tensile strength, but it also reduces maleability, increases brittleness and make fractures and breakages much more likely. To reduce these brittleness problems whilst still achieving high levels of hardness and tensile strength, low or medium carbon steels are alloyed with other metals. These alloy steels also require specific heat treatment to achieve the required mechanical properties, and the tensile strength/hardness trade off vs malleability remains, but to a much lesser extent compared to low alloy carbon steel. Alloying ingredients include chromium, molybdenum, silicon, manganese, nickel, and vanadium. The relative scarcity and high cost of these metals compared to iron is primarily what restricts their use.
Carbon steels which can successfully undergo heat-treatment have a carbon content in the range of 0.30–1.70% by weight. Trace impurities of various other elements can significantly affect the quality of the resulting steel. Trace amounts of sulfur in particular make the steel red-short, that is, brittle and crumbly at high working temperatures. Low-alloy carbon steel, such as A36 grade, contains about 0.05% sulfur and melt around. Manganese is often added to improve the hardenability of low-carbon steels. These additions turn the material into a low-alloy steel by some definitions, but AISI's definition of carbon steel allows up to 1.65% manganese by weight.
There are two types of higher carbon steels which are high carbon steel and the ultra high carbon steel. The reason for the limited use of high carbon steel is that it has extremely poor ductility and weldability and has a higher cost of production. The applications best suited for the high carbon steels is its use in the spring industry, farm industry, and in the production of wide range of high-strength wires.

Classification

Different classifications of non-alloy steel exist.

American AISI/SAE standard">SAE steel grades">AISI/SAE standard

Carbon steel is broken down into four classes based on carbon content:
  • Low-carbon steel has 0.05 to 0.15% carbon content.
  • Medium-carbon steel has approximately 0.3–0.5% carbon content. It balances ductility and strength and has good wear resistance. It is used for large parts, forging and automotive components.
  • High-carbon steels, for example 1075 and 1095 alloys, have approximately 0.6 to 1.0% carbon content. These steels are very strong, and are used for such products as springs, edged tools, and high-strength wires.
  • Ultra-high-carbon steels have approximately 1.25–2.0% carbon content. D2 steel with a content of 1.5% carbon falls into this category. UHC steels can be tempered to great hardness, and are used for special purposes such as knives, axles, and punches. Most steels with more than 2.5% carbon content are made using powder metallurgy.

    EN10020

EN 10020 categorizes non-alloy steels into two main groups:
  • Non-alloy quality steels: These are the most common type of non-alloy steels used for general structural purposes and are widely available. Their properties are guaranteed, but with broader tolerances than special steels. Examples include structural steels like S235, S275, and S355, which are defined in the EN 10025 standard.
  • Non-alloy special steels: These steels are made to a higher level of purity and have a more precisely controlled chemical composition. They're designed for applications that require consistent, specific properties, often achieved through heat treatments like quenching and tempering. An example would be steels used for machine parts or gears.

    Heat treatment

The purpose of heat treating carbon steel is to change the mechanical properties of steel, usually ductility, hardness, yield strength, or impact resistance. Note that the electrical and thermal conductivity are only slightly altered. As with most strengthening techniques for steel, Young's modulus is unaffected. All treatments of steel trade ductility for increased strength and vice versa. Iron has a higher solubility for carbon in the austenite phase; therefore all heat treatments, except spheroidizing and process annealing, start by heating the steel to a temperature at which the austenitic phase can exist. The steel is then quenched at a moderate to low rate allowing carbon to diffuse out of the austenite forming iron-carbide and leaving ferrite, or at a high rate, trapping the carbon within the iron thus forming martensite. The rate at which the steel is cooled through the eutectoid temperature affects the rate at which carbon diffuses out of austenite and forms cementite. Generally speaking, cooling swiftly will leave iron carbide finely dispersed and produce a fine grained pearlite and cooling slowly will give a coarser pearlite. Cooling a hypoeutectoid steel results in a lamellar-pearlitic structure of iron carbide layers with α-ferrite between. If it is hypereutectoid steel then the structure is full pearlite with small grains of cementite formed on the grain boundaries. A eutectoid steel will have a pearlite structure throughout the grains with no cementite at the boundaries. The relative amounts of constituents are found using the lever rule. The following is a list of the types of heat treatments possible:
; Spheroidizing: Spheroidite forms when carbon steel is heated to approximately for over 30 hours. Spheroidite can form at lower temperatures but the time needed drastically increases, as this is a diffusion-controlled process. The result is a structure of rods or spheres of cementite within primary structure. The purpose is to soften higher carbon steels and allow more formability. This is the softest and most ductile form of steel.
; Full annealing: A hypoeutectoid carbon steel is heated to approximately above the austenictic temperature, whereas a hypereutectoid steel is heated to a temperature above the eutectoid one for a certain number of hours; this ensures all the ferrite transforms into austenite. The steel must then be cooled slowly, in the realm of 20 °C per hour. Usually it is just furnace cooled, where the furnace is turned off with the steel still inside. This results in a coarse pearlitic structure, which means the "bands" of pearlite are thick. Fully annealed steel is soft and ductile, with no internal stresses, which is often necessary for cost-effective forming. Only spheroidized steel is softer and more ductile.
; Process annealing: A process used to relieve stress in a cold-worked carbon steel with less than 0.3% C. The steel is usually heated to for 1 hour, but sometimes temperatures as high as. The image above shows the process annealing area.
; Isothermal annealing: It is a process in which hypoeutectoid steel is heated above the upper critical temperature. This temperature is maintained for a time and then reduced to below the lower critical temperature and is again maintained. It is then cooled to room temperature. This method eliminates any temperature gradient.
; Normalizing: Carbon steel is heated to the austenitic region, ensuring the steel completely transforms to austenite, and then slow cooling in air. Normalizing steel is most often done to refine the grain structure, increase the strength relative to annealed steel, and/or to provide more uniform internal structure.
; Quenching: Carbon steel with at least 0.4 wt% C is heated to normalizing temperatures and then rapidly cooled in water, brine, or oil to the critical temperature. The critical temperature is dependent on the carbon content, but as a general rule is lower as the carbon content increases. This results in a martensitic structure; a form of steel that possesses a super-saturated carbon content in a deformed body-centered cubic crystalline structure, properly termed body-centered tetragonal, with much internal stress. Thus quenched steel is extremely hard but brittle, usually too brittle for practical purposes. These internal stresses may cause stress cracks on the surface. Quenched steel is approximately three times harder than normalized steel.
; Martempering : Martempering is not actually a tempering procedure, hence the term marquenching. It is a form of isothermal heat treatment applied after an initial quench, typically in a molten salt bath, at a temperature just above the "martensite start temperature". At this temperature, residual stresses within the material are relieved and some bainite may be formed from the retained austenite which did not have time to transform into anything else. In industry, this is a process used to control the ductility and hardness of a material. With longer marquenching, the ductility increases with a minimal loss in strength; the steel is held in this solution until the inner and outer temperatures of the part equalize. Then the steel is cooled at a moderate speed to keep the temperature gradient minimal. Not only does this process reduce internal stresses and stress cracks, but it also increases impact resistance.
; Tempering: This is the most common heat treatment encountered because the final properties can be precisely determined by the temperature and time of the tempering. Tempering involves reheating quenched steel to a temperature below the eutectoid temperature and then cooling. The elevated temperature allows very small amounts spheroidite to form, which restores ductility but reduces hardness. Actual temperatures and times are carefully chosen for each composition.
; Austempering: The austempering process is the same as martempering, except the quench is interrupted and the steel is held in the molten salt bath at temperatures between, and then cooled at a moderate rate. The resulting steel, called bainite, produces an acicular microstructure in the steel that has great strength, greater ductility, higher impact resistance, and less distortion than martensite steel. The disadvantage of austempering is it can be used only on a few sheets of steel, and it requires a special salt bath.